Method for producing semiconductor device and semiconductor device

ABSTRACT

A method for producing a semiconductor device includes a step of forming a first insulating film around a fin-shaped silicon layer and forming a pillar-shaped silicon layer in an upper portion of the fin-shaped silicon layer; a step of implanting an impurity into upper portions of the pillar-shaped silicon layer and fin-shaped silicon layer and a lower portion of the pillar-shaped silicon layer to form diffusion layers; and a step of forming a polysilicon gate electrode, a polysilicon gate line, and a polysilicon gate pad. The polysilicon gate electrode and the polysilicon gate pad have a larger width than the polysilicon gate line. After these steps follow a step of depositing an interlayer insulating film, exposing and etching the polysilicon gate electrode and the polysilicon gate line, and depositing a metal layer to form a metal gate electrode and a metal gate line, and a step of forming a contact.

RELATED APPLICATIONS

This application is a divisional patent application of U.S. patent application Ser. No. 13/891,655, filed May 10, 2013, which claims benefit pursuant to 35 U.S.C. §119(e) of U.S. Provisional Patent Application Ser. No. 61/648,817, filed May 18, 2012. The entire contents of which are hereby incorporated by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a method for producing a semiconductor device and a semiconductor device.

2. Description of the Related Art

Semiconductor integrated circuits, in particular, integrated circuits that use MOS transistors, are becoming more and more highly integrated. As the circuits achieve higher integration, the size of MOS transistors used therein is reduced to a nanometer range. With smaller MOS transistors, it sometimes becomes difficult to suppress leak current and to decrease the area occupied by the circuit since a particular amount of current is required. Under these circumstances, a surrounding gate transistor (hereinafter referred to as SGT), which includes a source, a gate, and a drain arranged in perpendicular to a substrate, the gate surrounding a pillar-shaped semiconductor layer, has been proposed (for example, refer to Japanese Unexamined Patent Application Publication Nos. 2-71556, 2-188966, and 3-145761).

Using a metal in the gate electrode instead of polysilicon helps suppress depletion and decrease the resistance of the gate electrode. However, this requires a production process that always takes into account metal contamination caused by the metal gate in the steps subsequent to formation of the metal gate.

To produce existing MOS transistors, a metal-gate-last process in which a metal gate is formed after a high temperature process is put into practice so as to avoid incompatibility between the metal gate process and the high temperature process (for example, refer to A 45 nm Logic Technology with High-k+Metal Gate Transistors, Strained Silicon, 9 Cu Interconnect Layers, 193 nm Dry Patterning, and 100% Pb-free Packaging, IEDM2007 K. Mistry et. al, pp 247-250).

That is, a MOS transistor has been made by forming a gate with polysilicon, depositing an interlayer insulating film on the polysilicon, exposing the polysilicon gate by chemical mechanical polishing (CMP), etching the polysilicon gate, and depositing a metal. In order to avoid incompatibility between the metal gate process and the high temperature process, it is also necessary for producing a SGT to employ a metal-gate-last process with which a metal gate is formed after a high temperature process. Since the upper part of a pillar-shaped silicon layer of a SGT is located at a position higher than the gate, some adjustment must be made in employing the metal-gate-last process.

An existing MOS transistor uses a first insulating film in order to decrease the parasitic capacitance between the gate line and the substrate. For example, in making a FINFET (refer to High performance 22/20 nm FinFET CMOS devices with advanced high-K/metal gate scheme, IEDM2010, C C. Wu, et. al, 27.1.1-27.1.4, for example), a first insulating film is formed around one fin-shaped semiconductor layer and then etched back so as to expose the fin-shaped semiconductor layer and to decrease the parasitic capacitance between the gate line and the substrate. In making a SGT also, a first insulating film is needed to reduce the parasitic capacitance between the gate line and the substrate. Since a SGT includes not only a fin-shaped semiconductor layer but also a pillar-shaped semiconductor layer, some adjustment must be made in order to form a pillar-shaped semiconductor layer.

According to a known SGT manufacturing process, a contact hole for a pillar-shaped silicon layer is formed by etching through a mask and then contact holes for a gate line and a planar silicon layer are formed by etching through a mask (for example, refer to Japanese Unexamined Patent Application Publication No. 2011-258780). That is, conventionally, two masks have been used for forming contacts.

SUMMARY OF THE INVENTION

The present invention has been made under the above-described circumstances. An object of the present invention is to provide a method for producing a semiconductor device, the method being a gate-last process capable of reducing the parasitic capacitance between a gate line and a substrate and uses only one mask for forming contacts, and to provide a semiconductor device obtained from the method.

A method for producing a semiconductor device according to a first aspect of the present invention includes:

a first step of forming a fin-shaped silicon layer on a silicon substrate, forming a first insulating film around the fin-shaped silicon layer, and forming a pillar-shaped silicon layer in an upper portion of the fin-shaped silicon layer so that a width of the pillar-shaped silicon layer is equal to a width of the fin-shaped silicon layer;

the second step of implanting an impurity to an upper portion of the pillar-shaped silicon layer, an upper portion of the fin-shaped silicon layer, and a lower portion of the pillar-shaped silicon layer to form diffusion layers, the second step being performed after the first step;

the third step of forming a gate insulating film, a polysilicon gate electrode, a polysilicon gate line, and a polysilicon gate pad so that the gate insulating film covers the periphery and an upper portion of the pillar-shaped silicon layer and the polysilicon gate electrode covers the gate insulating film, that, after the formation of the polysilicon gate electrode, the polysilicon gate line, and the polysilicon gate pad, an upper surface of the polysilicon is located at a position higher than the gate insulating film located on the diffusion layer in the upper portion of the pillar-shaped silicon layer, and that the width of the polysilicon gate electrode and the width of the polysilicon gate pad are larger than the width of the polysilicon gate line, the third step being performed after the second step;

the fourth step of forming a silicide in an upper portion of the diffusion layer in the upper portion of the fin-shaped silicon layer, the fourth step being performed after the third step;

the fifth step of depositing an interlayer insulating film, exposing the polysilicon gate electrode, polysilicon gate line, and the polysilicon gate pad, and etching the polysilicon gate electrode, polysilicon gate line, and the polysilicon gate pad, and depositing a metal layer so as to form a metal gate electrode, a metal gate line, and a metal gate pad, the metal gate line extending in a direction perpendicular to the fin-shaped silicon layer and being connected to the metal gate electrode, the fifth step being performed after the fourth step; and

the sixth step of forming a contact directly connected to the diffusion layer in the upper portion of the pillar-shaped silicon layer, the sixth step being performed after the fifth step.

Preferably, a first resist for forming the fin-shaped silicon layer on the silicon substrate is formed, the silicon substrate is etched by using the first resist so as to form the fin-shape silicon layer, and then the first resist is removed.

Preferably, the first insulating film is deposited around the fin-shaped silicon layer and the first insulating film is etched back to expose the upper portion of the fin-shaped silicon layer.

Preferably, a second resist is formed so as to perpendicularly intersect the fin-shaped silicon layer, the fin-shaped silicon layer is etched by using the second resist, and the second resist is removed so that the part where the fin-shaped silicon layer and the second resist intersect forms the pillar-shaped silicon layer.

Preferably, a second oxide film is deposited from above a structure that includes the fin-shaped silicon layer formed on the silicon substrate, the first insulating film formed around the fin-shaped silicon layer, and the pillar-shaped silicon layer formed in the upper portion of the fin-shaped silicon layer, a first nitride film is formed on the second oxide film, and the first nitride film is etched so as to be left as a sidewall.

Preferably, an impurity is then implanted so as to form the diffusion layers in the upper portion of the pillar-shaped silicon layer and the upper portion of the fin-shaped silicon layer, the first nitride film and the second oxide film are removed, and then a heat-treatment is performed.

In a structure that includes the fin-shaped silicon layer formed on the silicon substrate, the first insulating film formed around the fin-shaped silicon layer, the pillar-shaped silicon layer formed in the upper portion of the fin-shaped silicon layer, the diffusion layer formed in the upper portion of the fin-shaped silicon layer and the lower portion of the pillar-shaped silicon layer, and the diffusion layer formed in the upper portion of the pillar-shaped silicon layer,

preferably, a gate insulating film is formed, polysilicon is deposited and planarized, and an upper surface of the planarized polysilicon is located at a position higher than the gate insulating film on the diffusion layer in the upper portion of the pillar-shaped silicon layer; and

preferably, a second nitride film is deposited, a third resist for forming the polysilicon gate electrode, the polysilicon gate line, and the polysilicon gate pad is formed, the second nitride film and the polysilicon are etched by using the third resist so as to form the polysilicon gate electrode, the polysilicon gate line, and the polysilicon gate pad, the gate insulating film is etched, and then the third resist is removed.

Preferably, a third nitride film is deposited and etched so as to be left as a sidewall, a metal layer is deposited, and a silicide is formed in an upper portion of the diffusion layer in the upper portion of the fin-shaped silicon layer.

Preferably, a fourth nitride film is deposited, an interlayer insulating film is deposited and planarized, the polysilicon gate electrode, the polysilicon gate line, and the polysilicon gate pad are exposed, the polysilicon gate electrode, the polysilicon gate line, and the polysilicon gate pad are removed, and spaces where the polysilicon gate electrode, the polysilicon gate line, and the polysilicon gate pad had existed are filled with a metal, and the metal is etched to expose the gate insulating film on the diffusion layer in the upper portion of the pillar-shaped silicon layer and to form the metal gate electrode, the metal gate line, and the metal gate pad.

Preferably, a fifth nitride film thicker than a half of the width of the polysilicon gate line and thinner than a half of the width of the polysilicon gate electrode and a half of the width of the polysilicon gate pad is deposited to form contact holes on the pillar-shaped silicon layer and the metal gate pad.

A semiconductor device according to a second aspect of the present invention includes

a fin-shaped silicon layer formed on a silicon substrate;

a first insulating film formed around the fin-shaped silicon layer; a

pillar-shaped silicon layer formed on the fin-shaped silicon layer, the width of the pillar-shaped silicon layer being equal to the width of the fin-shaped silicon layer;

a diffusion layer formed in an upper portion of the fin-shaped silicon layer and in a lower portion of the pillar-shaped silicon layer;

a diffusion layer formed in an upper portion of the pillar-shaped silicon layer;

a silicide formed in an upper portion of the diffusion layer in the upper portion of the fin-shaped silicon layer;

a gate insulating film formed around the pillar-shaped silicon layer;

a metal gate electrode formed around the gate insulating film;

a metal gate line extending in a direction perpendicular to the fin-shaped silicon layer and being connected to the metal gate electrode;

a metal gate pad connected to the metal gate line, the width of the metal gate electrode and the width of the metal gate pad being larger than the width of the metal gate line; and

a contact formed on the diffusion layer formed in the upper portion of the pillar-shaped silicon layer,

in which the diffusion layer formed in the upper portion of the pillar-shaped silicon layer is directly connected to the contact.

According to the present invention, a method for producing a semiconductor device, the method being a gate-last process capable of reducing the parasitic capacitance between the gate line and the substrate and a semiconductor device produced through this method can be provided.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 2 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 3 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 4 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 5 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 6 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 7 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 8 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 9 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 10 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 11 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 12 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 13 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 14 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 15 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 16 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 17 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 18 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 19 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 20 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 21 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 22 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 23 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 24 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 25 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 26 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 27 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 28 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 29 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 30 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 31 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 32 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 33 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 34 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 35 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 36 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 37 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a);

FIG. 38 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a); and

FIG. 39 includes part (a) which is a plan view of a semiconductor device according to the present invention, part (b) which is a cross-sectional view taken along line X-X′ in (a), and part (c) which is a cross-sectional view taken along line Y-Y′ in (a).

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

A method for producing a semiconductor device according to an embodiment of the present invention and a semiconductor device obtained by the method will now be described with reference to drawings.

A production method that includes forming a fin-shaped silicon layer on a silicon substrate, forming a first insulating film around the fin-shaped silicon layer, and forming a pillar-shaped silicon layer in an upper portion of the fin-shaped silicon layer is described below.

First, as shown in FIG. 2, a first resist 102 for forming a fin-shaped silicon layer is formed on a silicon substrate 101.

Next, as shown in FIG. 3, the silicon substrate 101 is etched to form a fin-shaped silicon layer 103. Although a fin-shaped silicon layer is formed by using a resist as a mask here, a hard mask such as an oxide film or a nitride film may be used instead of the resist.

Next, as shown in FIG. 4, the first resist 102 is removed.

Then, as shown in FIG. 5, a first insulating film 104 composed of an oxide is formed around the fin-shaped silicon layer 103 by deposition. The first insulating film may be an oxide film formed by a high-density plasma process or an oxide film formed by a low-pressure chemical vapor deposition process instead of one made by such a deposition method.

As shown in FIG. 6, the first insulating film 104 is etched back to expose an upper portion of the fin-shaped silicon layer 103. The process up to here is the same as the process of making a fin-shaped silicon layer in PTL 2.

As shown in FIG. 7, a second resist 105 is formed to perpendicularly intersect the fin-shaped silicon layer 103. The part where the fin-shaped silicon layer 103 and the second resist 105 intersect forms a pillar-shaped silicon layer. Since a line-shaped resist can be used as such, the possibility of the break of the resist after formation of a pattern is low and the process becomes stable.

Then, as shown in FIG. 8, the fin-shaped silicon layer 103 is shaped by etching. As a result, the part where the fin-shaped silicon layer 103 and the second resist 105 intersect forms a pillar-shaped silicon layer 106. Accordingly, the width of the pillar-shaped silicon layer 106 is equal to the width of the fin-shaped silicon layer 103. As a result, a structure in which the pillar-shaped silicon layer 106 is formed in the upper portion of the fin-shaped silicon layer 103 and the first insulating film 104 is formed around the fin-shaped silicon layer 103 is formed.

As shown in FIG. 9, the second resist 105 is removed.

A method for forming diffusion layers by implanting an impurity into an upper portion of the pillar-shaped silicon layer, an upper portion of the fin-shaped silicon layer, and a lower portion of the pillar-shaped silicon layer is described below.

That is, as shown in FIG. 10, a second oxide film 107 is formed by deposition and a first nitride film 108 is formed. In order to prevent the impurity from being implanted into the sidewall of the pillar-shaped silicon layer, the first nitride film 108 need be formed only on the sidewall of the pillar-shaped silicon layer so as to have a sidewall shape. Since the upper part of the pillar-shaped silicon layer will be covered with a gate insulating film and a polysilicon gate electrode in the subsequent steps, it is desirable to form a diffusion layer in the upper portion of the pillar-shaped silicon layer before the pillar-shaped silicon layer is covered as such.

Then, as shown in FIG. 11, the first nitride film 108 is etched so as to be left as a sidewall.

Next, as shown in FIG. 12, an impurity such as arsenic, phosphorus, or boron is implanted to form a diffusion layer 110 in the upper portion of the pillar-shaped silicon layer and diffusion layers 109 and 111 in the upper portion of the fin-shaped silicon layer 103.

Then, as shown in FIG. 13, the first nitride film 108 and the second oxide film 107 are removed.

Referring now to FIG. 14, a heat-treatment is performed. The diffusion layers 109 and 111 in the upper portion of the fin-shaped silicon layer 103 come into contact with each other so as to form a diffusion layer 112. As a result of the above-described steps, an impurity is implanted into the upper portion of the pillar-shaped silicon layer 106, the upper portion of the fin-shaped silicon layer 103, and the lower portion of the pillar-shaped silicon layer 106 so as to form the diffusion layers 110 and 112.

A method for preparing a polysilicon gate electrode, a polysilicon gate line, and a polysilicon gate pad by using polysilicon will now be described. According to this method, an interlayer insulating film is first deposited and then a polysilicon gate electrode, a polysilicon gate line, and a polysilicon gate pad are exposed by chemical mechanical polishing (CMP). Thus, it is essential that the upper portion of the pillar-shaped silicon layer remain unexposed despite CMP.

In other words, as shown in FIG. 15, a gate insulating film 113 is formed, a polysilicon 114 is deposited, and the surface thereof is planarized. The upper surface of the polysilicon 114 after planarization is to come at a position higher than the gate insulating film 113 on the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106. In this manner, the upper portion of the pillar-shaped silicon layer can remain unexposed despite CMP, during which a polysilicon gate electrode 114 a, a polysilicon gate line 114 b, and a polysilicon gate pad 114 c become exposed and which is performed after deposition of the interlayer insulating film.

Next, a second nitride film 115 is deposited. The second nitride film 115 prevents formation of a silicide in the upper portions of the polysilicon gate electrode 114 a, polysilicon gate line 114 b, and polysilicon gate pad 114 c during the process of forming a silicide in the upper portion of the fin-shaped silicon layer 103.

Next, as shown in FIG. 16, a third resist 116 for forming the polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c is formed. The polysilicon gate pad 114 c is preferably arranged so that the part that forms a gate line perpendicularly intersects the fin-shaped silicon layer 103 in order to decrease the parasitic capacitance between the gate line and the substrate. The width of the polysilicon gate electrode 114 a and the width of the polysilicon gate pad 114 c are preferably larger than the width of the polysilicon gate line 114 b.

Then, as shown in FIG. 17, the second nitride film 115 is formed by etching.

Then, as shown in FIG. 18, the polysilicon 114 is etched to form the polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c.

Then, as shown in FIG. 19, the gate insulating film 113 is etched so as to remove the bottom portion of the gate insulating film 113.

Then, as shown in FIG. 20, the third resist 116 is removed.

The polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c are thus formed through the steps described above.

The upper surface of the polysilicon after forming the polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c is located at a position higher than the gate insulating film 113 on the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106.

A method for forming a silicide in the upper portion of the fin-shaped silicon layer will now be described. This method is characterized in that no silicide is formed in the upper portions of the polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c, and the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106. It is not preferable to form a silicide in the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106 since the number of steps in the method will increase.

First, as shown in FIG. 21, a third nitride film 117 is deposited.

Next, as shown in FIG. 22, the third nitride film 117 is etched to be left as a sidewall.

Then, as shown in FIG. 23, a metal such as nickel or cobalt is deposited to form a silicide 118 in the upper portion of the diffusion layer 112 in the upper portion of the fin-shaped silicon layer 103. Since the polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c are covered with the third nitride film 117 and the second nitride film 115 and the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106 is covered with the gate insulating film 113, the polysilicon gate electrode 114 a, and the polysilicon gate line 114 b, no silicide is formed in these parts.

Through the steps described above, a silicide is formed in the upper portion of the fin-shaped silicon layer 103.

Next, a gate-last production process in which, after an interlayer insulating film is deposited on the structure obtained through the steps described above, the polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c are exposed by CMP and removed by etching and then a metal is deposited is described.

First, as shown in FIG. 24, a fourth nitride film 119 is deposited to protect the silicide 118.

Next, as shown in FIG. 25, an interlayer insulating film 120 is deposited and the surface thereof is planarized by CMP.

Then, as shown in FIG. 26, the polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c are exposed by CMP.

Then, as shown in FIG. 27, the polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c are etched. They are preferably wet-etched.

Then, as shown in FIG. 28, a metal 121 is deposited and the surface thereof is planarized so as to fill the spaces where the polysilicon gate electrode 114 a, the polysilicon gate line 114 b, and the polysilicon gate pad 114 c had existed with the metal 121. Atomic layer deposition is preferably employed to fill the spaces.

Then, as shown in FIG. 29, the metal 121 is etched to expose the gate insulating film 113 on the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106. As a result, a metal gate electrode 121 a, a metal gate line 121 b, and a metal gate pad 121 c are formed.

The steps described above constitute the method for producing a semiconductor device by a gate-last technique of depositing metal layers after etching the polysilicon gate exposed by CMP after deposition of the interlayer insulating film.

A method for forming contacts will now be described. Here, since no silicide is formed in the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106, the contact is directly connected to the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106.

That is, first, as shown in FIG. 30, a fifth nitride film 122 is deposited so that the fifth nitride film 122 is thicker than a half of the width of the polysilicon gate line 114 b and thinner than a half of the width of the polysilicon gate electrode 114 a and a half of the width of the polysilicon gate pad 114 c. As a result, contact holes 123 and 124 are formed on the pillar-shaped silicon layer 106 and the metal gate pad 121 c. The fifth nitride film 122 and the gate insulating film 113 at the bottom portions of the contact holes 123 and 124 will be removed by a subsequent step of etching the nitride film. Accordingly, a mask for forming the contact hole 123 on the pillar-shaped silicon layer and the contact hole 124 on the metal gate pad 121 c is not needed.

Next, as shown in FIG. 31, a fourth resist 125 for forming a contact hole 126 on the fin-shaped silicon layer 103 is formed.

Then, as shown in FIG. 32, the fifth nitride film 122 and the interlayer insulating film 120 are etched to form the contact hole 126.

Then, as shown in FIG. 33, the fourth resist 125 is removed.

Then, as shown in FIG. 34, the fifth nitride film 122, the fourth nitride film 119, and the gate insulating film 113 are etched to expose the silicide 118 and the diffusion layer 110.

Then, as shown in FIG. 35, a metal is deposited to form contacts 127, 128, and 129.

Through the steps described above, the contacts 127, 128, and 129 can be formed in the semiconductor device. According to this production method, no silicide is formed in the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106 and thus the contact 128 is directly connected to the diffusion layer 110 in the upper portion of the pillar-shaped silicon layer 106.

The method for forming metal wiring layers will now be described.

First, as shown in FIG. 36, a metal 130 is deposited.

Next, as shown in FIG. 37, fifth resists 131, 132, and 133 for forming metal wirings are formed.

Then, as shown in FIG. 38, the metal 130 is etched to form metal wirings 134, 135, and 136.

Then, as shown in FIG. 39, the fifth resists 131, 132, and 133 are removed.

Through the steps described above, the metal wirings 134, 135, and 136 which constitute metal wiring layers are formed.

A semiconductor device produced by the production method described above is shown in FIG. 1.

The semiconductor device shown in FIG. 1 includes the fin-shaped silicon layer 103 formed on the silicon substrate 101, the first insulating film 104 formed around the fin-shaped silicon layer 103, the pillar-shaped silicon layer 106 formed on the fin-shaped silicon layer 103, the width of the pillar-shaped silicon layer 106 being equal to the width of the fin-shaped silicon layer 103, and the diffusion layer 112 formed in the upper portion of the fin-shaped silicon layer 103 and in the lower portion of the pillar-shaped silicon layer 106.

The semiconductor device shown in FIG. 1 further includes the diffusion layer 110 formed in the upper portion of the pillar-shaped silicon layer 106, the silicide 118 formed in the upper portion of the diffusion layer 112 in the upper portion of the fin-shaped silicon layer 103, the gate insulating film 113 formed around the pillar-shaped silicon layer 106, the metal gate electrode 121 a formed around the gate insulating film, the metal gate line 121 b extending in a direction perpendicular to the fin-shaped silicon layer 103 and being connected to the metal gate electrode 121 a, and the metal gate pad 121 c connected to the metal gate line 121 b. The width of the metal gate electrode 121 a and the width of the metal gate pad 121 c are larger than the width of the metal gate line 121 b.

The semiconductor device shown in FIG. 1 has a structure in which the contact 128 is formed on the diffusion layer 110 and the diffusion layer 110 is directly connected to the contact 128.

In sum, according to this embodiment of the present invention, a method for producing a SGT, which is a gate-last process capable of decreasing the parasitic capacitance between the gate line and the substrate and which uses only one mask for forming contacts is provided. A SGT structure obtained by this method is also provided.

Since the method for producing a semiconductor device of the embodiment is based on a known method for producing FINFET, the fin-shaped silicon layer 103, the first insulating film 104, and the pillar-shaped silicon layer 106 can be easily formed.

According to a known method, a silicide is formed in the upper portion of a pillar-shaped silicon layer. Since the polysilicon deposition temperature is higher than the temperature for forming the silicide, the silicide needs to be formed after forming the polysilicon gate. Thus, in the case where a silicide is to be formed in the upper portion of a silicon pillar, the steps of forming a polysilicon gate, forming a hole in the upper portion of the polysilicon gate electrode, forming a sidewall with an insulating film on the sidewall of that hole, forming a silicide, and filling the hole with an insulating film are needed. Thus, there is a problem in that the number of steps in the method will increase.

In contrast, according to the embodiment described above, diffusion layers are formed before forming the polysilicon gate electrode 114 a and the polysilicon gate line 114 b and the pillar-shaped silicon layer 106 is covered with the polysilicon gate electrode 114 a so that the silicide is formed in the upper portion of the fin-shaped silicon layer 103 only. Then a gate is formed with a polysilicon, the interlayer insulating film 120 is deposited, the polysilicon gate is exposed by chemical mechanical polishing (CMP), and then the polysilicon gate is etched, followed by deposition of a metal. Such a metal-gate-last production method can be used in this embodiment. Thus, according to this method for producing a semiconductor device, a SGT having a metal gate can be easily produced.

The width of the polysilicon gate electrode 114 a and the width of the polysilicon gate pad 114 c are larger than the width of the polysilicon gate line 114 b. Furthermore, the fifth nitride film 122 thicker than a half of the width of the polysilicon gate line 114 b and thinner than a half of the width of the polysilicon gate electrode 114 a and a half of the width of the polysilicon gate pad 114 c are deposited in a hole formed by etching the polysilicon gate after forming the metal gate. Thus, the contact holes 123 and 124 can be formed on the pillar-shaped silicon layer 106 and the metal gate pad 121 c, and thus a conventionally required etching step that forms a contact hole in the pillar-shaped silicon layer through a mask is no longer needed. In other words, only one mask is needed to form contacts.

It should be understood that various other embodiments and modifications are possible without departing from the spirit and scope of the present invention in a broad sense. The embodiment described above is merely illustrative and does not limit the scope of the present invention. 

1.-7. (canceled)
 8. A semiconductor device comprising: a fin-shaped silicon layer formed on a silicon substrate; a first insulating film formed around the fin-shaped silicon layer; a pillar-shaped silicon layer formed on the fin-shaped silicon layer, the width of the pillar-shaped silicon layer being equal to the width of the fin-shaped silicon layer; a diffusion layer formed in an upper portion of the fin-shaped silicon layer and in a lower portion of the pillar-shaped silicon layer; a diffusion layer formed in an upper portion of the pillar-shaped silicon layer; a silicide formed in an upper portion of the diffusion layer in the upper portion of the fin-shaped silicon layer; a gate insulating film formed around the pillar-shaped silicon layer; a metal gate electrode formed around the gate insulating film; a metal gate line extending in a direction perpendicular to the fin-shaped silicon layer and being connected to the metal gate electrode; a metal gate pad connected to the metal gate line, the width of the metal gate electrode and the width of the metal gate pad being larger than the width of the metal gate line; and a contact formed on the diffusion layer formed in the upper portion of the pillar-shaped silicon layer, wherein the diffusion layer formed in the upper portion of the pillar-shaped silicon layer is directly connected to the contact. 